Реферат: Two types of the low temperature WGS catalysts were compared: oxide Cu-Zn-Al catalyst prepared through coprecipitation procedure and ceramometal CuAlO/CuA catalyst prepared from powdered CuAl alloy. The catalysts were characterized by XRD, SEM with EDX, adsorption-desorption isotherms. Activity was measured at a pressure of 1 bar in the mixture of CO:Н2О:Н2 = 8:42:50 at a steam/gas ratio of 0.6–0.7. The catalysts were used as a small (0.14–0.25 mm) and large (3.2 × 3.2 × 5 mm) fraction. It was found that oxide catalyst possesses of a developed mesopore structure with specific surface area 122 m2/g while ceramometal catalyst has a developed macropore structure with size up to ten microns and specific surface area 15.7 m2/g. As a result, large fraction (granules) of ceramometal catalyst has twofold higher effectiveness factor due to higher internal diffusion.

Библиографическая ссылка: Tikhov S.F. , Minyukova T.P. , Reshetnikov S.I. , Valeev K.R. , Vernikovskaya N.V. , Salanov A.N. , Cherepanova S.V. , Sadykov V.A.
Particularities of low-temperature WGSR over ceramometal and oxide catalysts: Effect of catalyst particle size
Chemical Engineering Journal. 2019. V.374. P.405-411. DOI: 10.1016/j.cej.2019.05.089 WOS Scopus OpenAlex

Даты:

Опубликована online:

16 мая 2019 г.

Идентификаторы БД:

Web of science:	WOS:000477652900038
Scopus:	2-s2.0-85066295528
OpenAlex:	W2944838526

Цитирование в БД:

БД	Цитирований
OpenAlex	9
Scopus	8

Альметрики: