X-Ray Diffraction Study of Zirconia Pillared Clays Научная публикация
| Журнал |
Reaction Kinetics and Catalysis Letters
ISSN: 0133-1736 , E-ISSN: 1588-2837 |
||
|---|---|---|---|
| Вых. Данные | Год: 2004, Том: 81, Номер: 1, Страницы: 137-142 Страниц : 6 DOI: 10.1023/B:REAC.0000016527.92435.63 | ||
| Авторы |
|
||
| Организации |
|
Реферат:
X-ray powder diffraction (XRPD) and X-ray radial electronic distribution density (RED) of initial and zirconia-pillared interlayered clays (Zr-PILC) were studied. After pillaring, the basal (001) spacing was found to increase from 11 Å in the initial clay kept under air to 17.7 Å in Zr-PILC. The structure of zirconium nanopillars was characterized. The interatomic distances with corresponding coordination numbers obtained from the RED curves were close to those in zirconium tetramers.
Библиографическая ссылка:
Zyuzin D.A.
, Moroz E.M.
, Kuznetsova T.G.
, Sadykov V.A.
, Doronin V.P.
X-Ray Diffraction Study of Zirconia Pillared Clays
Reaction Kinetics and Catalysis Letters. 2004. V.81. N1. P.137-142. DOI: 10.1023/B:REAC.0000016527.92435.63 WOS Scopus РИНЦ CAPlusCA OpenAlex Sciact
X-Ray Diffraction Study of Zirconia Pillared Clays
Reaction Kinetics and Catalysis Letters. 2004. V.81. N1. P.137-142. DOI: 10.1023/B:REAC.0000016527.92435.63 WOS Scopus РИНЦ CAPlusCA OpenAlex Sciact
Даты:
| Поступила в редакцию: | 26 сент. 2003 г. |
| Принята к публикации: | 29 сент. 2003 г. |
| Опубликована в печати: | 1 янв. 2004 г. |
Идентификаторы БД:
| Web of science: | WOS:000189353900018 |
| Scopus: | 2-s2.0-1542336742 |
| РИНЦ: | 13472356 |
| Chemical Abstracts: | 2004:131865 |
| Chemical Abstracts (print): | 140:345333 |
| OpenAlex: | W2095396884 |
| Sciact: | 10904 |