Reinforced Nickel Catalysts for Steam Reforming of Methane to Synthesis Gas Научная публикация
| Журнал |
Reaction Kinetics and Catalysis Letters
ISSN: 0133-1736 , E-ISSN: 1588-2837 |
||
|---|---|---|---|
| Вых. Данные | Год: 2009, Том: 97, Номер: 2, Страницы: 363-370 Страниц : 8 DOI: 10.1007/s11144-009-0042-0 | ||
| Авторы |
|
||
| Организации |
|
Реферат:
XRD, mercury porosimetry, low-temperature nitrogen adsorption and electron microscopy were used to study peculiarities of the formation of reinforced composite nickel catalysts. The catalysts were prepared by sintering powdered metallic nickel with a supported nickel catalyst (GIAP-3 or NIAP-18) applied to a reinforcing stainless steel gauze. It was found that a metal matrix, in the pores of which supported catalyst particles were distributed, was formed in the composite catalysts. The NIAP-18-based catalyst exceeded the GIAP-3-based catalyst in activity toward the methane steam reforming. The NIAP-18-based catalyst was as active as the Cr2O3-doped NIAP-18-based catalyst, but showed a worse coke-resistance. A chromium oxide additive increased the activity of the GIAP-3-based catalyst.
Библиографическая ссылка:
Sabirova Z.A.
, Danilova M.M.
, Kuzin N.A.
, Kirillov V.A.
, Zaikovskii V.I.
, Krieger T.A.
Reinforced Nickel Catalysts for Steam Reforming of Methane to Synthesis Gas
Reaction Kinetics and Catalysis Letters. 2009. V.97. N2. P.363-370. DOI: 10.1007/s11144-009-0042-0 WOS Scopus РИНЦ CAPlusCA OpenAlex Sciact
Reinforced Nickel Catalysts for Steam Reforming of Methane to Synthesis Gas
Reaction Kinetics and Catalysis Letters. 2009. V.97. N2. P.363-370. DOI: 10.1007/s11144-009-0042-0 WOS Scopus РИНЦ CAPlusCA OpenAlex Sciact
Даты:
| Поступила в редакцию: | 11 дек. 2008 г. |
| Принята к публикации: | 20 апр. 2009 г. |
| Опубликована online: | 11 июл. 2009 г. |
| Опубликована в печати: | 1 авг. 2009 г. |
Идентификаторы БД:
| Web of science: | WOS:000268445800028 |
| Scopus: | 2-s2.0-68249127200 |
| РИНЦ: | 22124839 |
| Chemical Abstracts: | 2009:915350 |
| Chemical Abstracts (print): | 153:264429 |
| OpenAlex: | W2060029038 |
| Sciact: | 3049 |